Hastelloy G-30
ASME SB622, ASME SB626, ASME SB366, UNS N06030, ASME SB581, ASME SB582, ASME SB619 |
                              Chemical Requirement
Chemistry (% Wt.) |
Type |
UNS # |
C |
Ni |
Cr |
Fe |
Mo |
Other |
G-30 |
N06030 |
0.03max |
Rem |
28.0-31.5 |
13.0-17.0 |
4.0-6.0 |
5.0maxCo;1-2.4Cu
0.3-1.5Cb |
|
|
Material Notes:
Nickel content to balance. Cb and Ta content = 0.3-1.5%. Superior corrosion resistance to commercial phosphoric acids and oxidizing acid mixtures. Typical applications include phosphoric acid service, sulfuric acid service, nitric acid service, nuclear fuel reprocessing, nuclear waste processing, pickling operations, petrochemicals, fertilizer manufacture, pesticide manufacture, and gold ore extraction. |
| |
Physical Properties |
Metric |
English |
Comments |
|
Density |
8.22 g/cc |
0.297 lb/in³ |
 at 22°C (72°F) |
Mechanical Properties
|
|
Hardness, Brinell |
128 |
128 |
 Converted from Rockwell B hardness. |
Hardness, Knoop |
172 |
172 |
 Converted from Rockwell B hardness. |
Hardness, Rockwell B |
90 |
90 |
 |
Hardness, Vickers |
191 |
191 |
 Converted from Rockwell B hardness. |
Tensile Strength, Ultimate |
690 MPa |
100000 psi |
 |
Tensile Strength, Yield |
317 MPa |
46000 psi |
 at 0.2% offset |
Elongation at Break |
64 % |
64 % |
 in 50.8 mm |
|
 |
|
|